It
is well known that a material subjected to a cyclic
load far below the ultimate tensile stress can fail,
a process called fatigue. If the metal is simultaneously
exposed to a corrosive environment, the failure can
take place at even lower loads and after a shorter time.
Contrary to a pure mechanical fatigue, there is no fatigue
limit load in corrosion-assisted fatigue.